Liquid crystal alignment film, method for preparing the same and liquid crystal display device using the same

ABSTRACT

The present invention provides a liquid crystal alignment film not only having an excellent alignment property and stability, but also having high film strength, and thus exhibiting excellent durability and a high residual image property, a method for preparing the same, and a liquid crystal display device using the same.

CROSS-REFERENCE TO RELATED APPLICATION(S)

This application claims priority to and the benefit of Korean Patent Application No. 10-2016-0159597 filed on Nov. 28, 2016 and Korean Patent Application No. 10-2017-0134828 filed on Oct. 17, 2017 with the Korean Intellectual Property Office, the disclosures of which are incorporated herein by reference in their entirety.

TECHNICAL FIELD

The present invention relates to a liquid crystal alignment film having not only an excellent alignment property and stability, but also having high film strength, and thus exhibiting excellent durability and high residual image property, and a liquid crystal display device using the same.

BACKGROUND ART

In a liquid crystal display device, a liquid crystal alignment film plays a role of aligning liquid crystals in a certain direction. Specifically, a liquid crystal alignment film serves as a director in the arrangement of liquid crystal molecules, and thus, when the liquid crystals move by the electric field to form an image, it helps them to move in an appropriate direction. Generally, in order to obtain uniform brightness and a high contrast ratio in a liquid crystal display device, it is essential that the liquid crystals are uniformly aligned.

As a conventional method for aligning liquid crystals, a rubbing method of coating a polymer film such as a polyimide onto a substrate such as glass or the like and rubbing the surface thereof in a predetermined direction using fibers such as nylon or polyester has been used. However, the rubbing method may cause serious problems during manufacturing of a liquid crystal panel because fine dust or electrostatic discharge (ESD) occurs when the fiber and polymer film are rubbed.

In order to solve the problems of the rubbing method, a photo-alignment method for inducing anisotropy in a polymer film by light irradiation rather than the rubbing, and aligning liquid crystals using anisotropy, has been studied recently.

As materials that can be used for the photo-alignment method, various materials have been introduced, among which a polyimide is mainly used for various superior performance of a liquid crystal alignment film. However, a common polyimide is usually poor in solubility in a solvent, and so it is difficult to apply it directly to a manufacturing process for forming an alignment film by coating in a solution state. Accordingly, after coating in the form of a precursor such as a polyamic acid or a polyamic acid ester having excellent solubility, a high-temperature heat treatment process is performed to form the polyimide, which is then subjected to light irradiation to align liquid crystals.

However, as a large amount of energy is required for obtaining sufficient liquid crystal alignment properties by subjecting the film in the form of a polyimide to light irradiation, it is difficult to secure substantial productivity, and additionally, there is a limitation that an additional heat treatment process is required for securing alignment stability after the light irradiation.

DETAILED DESCRIPTION OF THE INVENTION Technical Problem

It is one object of the present invention to provide a liquid crystal alignment film having not only excellent alignment property and stability, but also having high film strength, and thus exhibiting excellent durability and a high residual image property.

It is another object of the present invention to provide a method for preparing a liquid crystal alignment film having not only excellent alignment property and stability, but also having high film strength, and further having enhanced electrical characteristics such as voltage holding ratio.

It is still another object of the present invention to provide a liquid crystal display device including the liquid crystal alignment film.

Technical Solution

In order to achieve the objects above, the present invention provides a liquid crystal alignment film including: a polymer containing a first repeating unit including at least one selected from the group consisting of Chemical Formula 1 to Chemical Formula 3 below; and a second repeating unit including at least one selected from the group consisting of Chemical Formula 4 and Chemical Formula 5 below, wherein the liquid crystal alignment film has a retardation value of 3 nm or higher:

wherein, in Chemical Formulae 1 to 5,

at least one of R¹ and R² is an alkyl group having 1 to 10 carbon atoms and the other is hydrogen, and

X¹ to X⁵ are each independently a tetravalent organic group represented by Chemical Formula 6 below:

wherein, in Chemical Formula 6,

R³ to R⁸ are each independently hydrogen or an alkyl group having 1 to 10 carbon atoms,

L¹ is any one selected from the group consisting of a direct bond, —O—, —CO—, —COO—, —S—, —SO—, —CR⁹R¹⁰—, —(CH₂)_(Z)—, —O(CH₂)_(Z)O—, —COO(CH₂)_(Z)OCO—, —CONH—, phenylene, or a combination thereof,

wherein R⁹ and R¹⁰ are each independently hydrogen, an alkyl group having 1 to 10 carbon atoms, or a fluoroalkyl group,

Z is an integer of 1 to 10, and

Y¹ to Y⁵ are each independently a divalent organic group represented by Chemical Formula 7 below:

wherein, in Chemical Formula 7,

A is a tetravalent organic group represented by Chemical Formula 6,

D¹ and D² are each independently an arylene group having 6 to 20 carbon atoms; and

in Chemical Formulae 4 and 5,

at least one of R′ and R″ is a functional group containing a mesogenic group in the molecule, and the other is hydrogen.

As described above, the liquid crystal alignment film according to the present invention includes the second repeating unit formed by reacting a common polyimide or a precursor repeating unit thereof with a reactive mesogenic epoxy additive, together with the first repeating unit including a common polyimide or a precursor repeating unit thereof, thereby preparing an alignment film having excellent film strength and good aligning properties.

In particular, in the first repeating unit and the second repeating unit, each divalent organic group represented by Chemical Formula 7 is independently used for Y¹ to Y⁵ functional groups derived from diamine, and thus the polymer including the first repeating unit can have anisotropy by UV exposure.

Herein, in the second repeating unit, through the anisotropy obtained during UV exposure by the divalent organic group represented by Chemical Formula 7, liquid crystal alignment is carried out from the mesogenic group-containing functional group included in the second repeating unit, thereby improving liquid crystal aligning performance. In addition, the mesogenic group-containing functional group in the second repeating unit can improve the film strength while forming a bond through the reaction with the polyimide or a precursor thereof.

More specifically, the liquid crystal alignment film according to the present invention can be prepared by a method for preparing a liquid crystal alignment film including the steps of: 1) coating a liquid crystal aligning agent composition onto a substrate to form a coating film; 2) drying the coating film; 3) irradiating the coating film immediately after the drying step with light to perform alignment treatment; 4) subjecting the alignment-treated coating film to low-temperature heat treatment at 200° C. or lower; and 5) subjecting the heat-treated coating film to heat treatment at a higher temperature than that of the low-temperature heat treatment to cure it, wherein the liquid crystal aligning agent composition includes: i) a first polymer for a liquid crystal aligning agent including at least two repeating units selected from the group consisting of a repeating unit represented by Chemical Formula 21 below, a repeating unit represented by Chemical Formula 22 below, and a repeating unit represented by Chemical Formula 23 below, wherein the repeating unit represented by Chemical Formula 21 below is contained in an amount of 5 mol % to 74 mol % relative to the entire repeating units represented by Chemical Formulae 21 to 23 below; ii) a second polymer for a liquid crystal aligning agent including a repeating unit represented by Chemical Formula 24 below; and iii) a reactive mesogenic epoxy:

wherein, in Chemical Formulae 21 to 24,

R²² and R²³ are each independently hydrogen or a C₁₋₁₀ alkyl, with the proviso that R²² and R²³ are not all hydrogen,

R²⁴ and R²⁵ are each independently hydrogen or a C₁₋₁₀ alkyl, and

X¹¹ is a tetravalent organic group represented by Chemical Formula 25 below:

wherein, in Chemical Formula 25,

R²⁶ to R²⁹ are each independently hydrogen or a C₁₋₆ alkyl,

X¹², X¹³, and X¹⁴ are each independently a tetravalent organic group derived from a hydrocarbon having 4 to 20 carbon atoms, or a tetravalent organic group in which at least one hydrogen in the tetravalent organic groups is substituted with a halogen or in which at least one —CH₂— is substituted with —O—, —CO—, —S—, —SO—, —SO₂—, or —CONH—, so that it may not be directly bonded to oxygen or sulfur atoms, and

Y¹¹, Y¹², Y¹³, and Y¹⁴ are each independently a divalent organic group represented by Chemical Formula 26 below:

wherein, in Chemical Formula 26,

R³⁰ and R³¹ are each independently a halogen, a cyano, a C₁₋₁₀ alkyl, a C₂₋₁₀ alkenyl, a C₁₋₁₀ alkoxy, a C₁₋₁₀ fluoroalkyl, or a C₁₋₁₀ fluoroalkoxy,

h and i are each independently an integer of 0 to 4,

L³ is a single bond, —O—, —CO—, —S—, —C(CH₃)₂—, —C(CF₃)₂—, —CONH—, —COO—, —(CH₂)_(z)—, —O(CH₂)_(z)O—, —O(CH₂)_(z)—, —OCH₂—C(CH₃)₂—CH₂O—, —COO—(CH₂)_(z)—OCO—, —OCO—(CH₂)_(z)—COO—, or an imide-based functional group,

z is an integer of 1 to 10, and

j is an integer of 0 to 3.

In general, it is known that when a reactive mesogenic epoxy is included in a liquid crystal aligning agent, the film strength of an alignment film is enhanced. It is also known that as the content thereof increases, the film strength increases. However, when the content of the reactive mesogenic epoxy increases, there is a problem that the residual image property while driving a liquid crystal device is induced. This is because, although the content thereof is not theoretically limited, the alignment of a liquid crystal aligning agent is carried out at a high temperature, and thus the alignment of the liquid crystal aligning agent and the reaction of the epoxy included in the reactive mesogenic epoxy are carried out at the same time.

Accordingly, in the present invention, the liquid crystal aligning agent composition according to the present invention is coated onto a substrate and dried to form a film, which is then immediately irradiated with linearly polarized light without an imidization process to induce initial anisotropy, and subsequently, alignment of the reactive mesogenic epoxy present in the alignment film is initially induced through a low-temperature heat treatment, followed by carrying out an epoxy reaction to prepare a reactive mesogenic liquid crystal film in the alignment film. Then, while carrying out a high-temperature heat treatment at a higher temperature than that of the low-temperature heat treatment to thereby proceed with imidization, the alignment stabilization can be achieved due to the anisotropy of the liquid crystal film prepared in the low-temperature heat treatment process. Accordingly, it is possible to prevent the occurrence of the residual image property while enhancing the film strength by using the reactive mesogenic epoxy.

The liquid crystal alignment film prepared according to the method for preparing a liquid crystal alignment as described above not only exhibits excellent alignment properties, but also has an excellent high-temperature AC brightness fluctuation rate, and in addition, it has a feature in that it can maintain a high voltage holding ratio for a long period of time.

Hereinafter, the present invention will be described in detail for each component.

Definition of Terms

Unless specified otherwise herein, the following terms can be defined as follows.

The hydrocarbon having 4 to 20 carbon atoms may be an alkane having 4 to 20 carbon atoms, an alkene having 4 to 20 carbon atoms, an alkyne having 4 to 20 carbon atoms, a cycloalkane having 4 to 20 carbon atoms, a cycloalkane having 4 to 20 carbon atoms, an arene having 6 to 20 carbon atoms, or a fused ring in which at least one of the cyclic hydrocarbons shares two or more atoms, or a hydrocarbon to which at least one of the hydrogens is chemically bonded. Specifically, examples of the hydrocarbon having 4 to 20 carbon atoms may include n-butane, cyclobutane, 1-methylcyclobutane, 1,3-dimethylcyclobutane, 1,2,3,4-tetramethylcyclobutane, cyclopentane, cyclohexane, cycloheptane, cyclooctane, cyclohexene, 1-methyl-3-ethylcyclohexene, bicyclohexyl, benzene, biphenyl, diphenylmethane, 2,2-diphenylpropane, 1-ethyl-1,2,3,4-tetrahydronaphthalene, or 1,6-diphenylhexane, etc.

The alkyl group having 1 to 10 carbon atoms may be a straight-chain, branched-chain, or cyclic alkyl group. Specifically, the alkyl group having 1 to 10 carbon atoms may be a straight-chain alkyl group having 1 to 10 carbon atoms; a straight-chain alkyl group having 1 to 5 carbon atoms; a branched-chain or cyclic alkyl group having 3 to 10 carbon atoms; or a branched-chain or cyclic alkyl group having 3 to 6 carbon atoms. More specifically, examples of the alkyl group having 1 to 10 carbon atoms may include a methyl group, an ethyl group, an n-propyl group, an isopropyl group, an n-butyl group, an iso-butyl group, a tert-butyl group, an n-pentyl group, an iso-pentyl group, a neo-pentyl group, a cyclohexyl group, etc.

The alkoxy group having 1 to 10 carbon atoms may be a straight-chain, branched-chain, or cyclic alkoxy group. Specifically, the alkoxy group having 1 to 10 carbon atoms may be a straight-chain alkoxy group having 1 to 10 carbon atoms; a straight-chain alkoxy group having 1 to 5 carbon atoms; a branched-chain or cyclic alkoxy group having 3 to 10 carbon atoms; or a branched-chain or cyclic alkoxyl group having 3 to 6 carbon atoms. More specifically, examples of the alkoxy group having 1 to 10 carbon atoms may include a methoxy group, an ethoxy group, an n-propoxy group, an iso-propoxy group, an n-butoxy group, an iso-butoxy group, a tert-butoxy group, an n-pentoxy group, an iso-pentoxy group, a neo-pentoxy group, a cyclohexoxy group, etc.

The fluoroalkyl group having 1 to 10 carbon atoms may be a group in which at least one hydrogen in the alkyl group having 1 to 10 carbon atoms is substituted with fluorine, and the fluoroalkoxy group having 1 to 10 carbon atoms may be a group in which at least one hydrogen in the alkoxy group having 1 to 10 carbon atoms is substituted with fluorine.

The alkenyl group having 2 to 10 carbon atoms may be a straight-chain, branched-chain, or cyclic alkenyl group. Specifically, the alkenyl group having 2 to 10 carbon atoms may be a straight-chain alkenyl group having 2 to 10 carbon atoms, a straight-chain alkenyl group having 2 to 5 carbon atoms, a branched-chain alkenyl group having 3 to 10 carbon atoms, a branched-chain alkenyl group having 3 to 6 carbon atoms, a cyclic alkenyl group having 5 to 10 carbon atoms, or a cyclic alkenyl group having 6 to 8 carbon atoms. More specifically, examples of the alkenyl group having 2 to 10 carbon atoms may include an ethenyl group, a propenyl group, a butenyl group, a pentenyl group, a cyclohexenyl group, etc.

The halogen may be fluorine (F), chlorine (Cl), bromine (Br), or iodine (I).

In the present specification, an aryl group is not particularly limited, but an aryl group having 6 to 60 carbon atoms is preferred, and it may be a monocyclic aryl group or a polycyclic aryl group. According to one embodiment, the aryl group has a carbon number of 6 to 30. According to one embodiment, the aryl group has a carbon number of 6 to 20. The monocyclic aryl group may be a phenyl group, a biphenyl group, a terphenyl group, and the like, but is not limited thereto. The polycyclic aryl group may be a naphthyl group, an anthracenyl group, a phenanthryl group, a pyrenyl group, a perylenyl group, a chrycenyl group, a fluorenyl group, and the like, but is not limited thereto.

In the present specification, an alkylene group is a divalent functional group derived from an alkane, and examples thereof may include a straight-chain, branched-chain, or cyclic-chain of a methylene group, an ethylene group, a propylene group, an isobutylene group, a sec-butylene group, a tert-butylene group, a pentylene group, a hexylene group, and the like.

In the present specification, an arylene group refers to a group having two bonding sites in the aryl group, that is, a divalent group. The description of the aryl group described above can be applied, except that each of these is a divalent group.

The multivalent organic group derived from an arbitrary compound refers to a residue in which a plurality of hydrogen atoms bonded to the arbitrary compound are removed. In one example, a tetravalent organic group derived from cyclobutane refers to a residue in which any four hydrogen atoms bonded to cyclobutane are removed.

In the present specification, the notation —* refers to a residue in which hydrogens at the relevant site are removed. For example, the notation

refers to a residue in which four hydrogen atoms bonded to carbon numbers 1, 2, 3, and 4 of cyclobutane are removed, that is, it refers to any one of tetravalent organic groups derived from cyclobutane. In the present specification, a direct bond means that no other atoms are present in the parts represented as L¹, L², L, and the like.

Liquid Crystal Alignment Film

The liquid crystal alignment film of one embodiment may include a polymer containing a first repeating unit including at least one selected from the group consisting of Chemical Formula 1 to Chemical Formula 3; and a second repeating unit including at least one selected from the group consisting of Chemical Formula 4 and Chemical Formula 5.

That is, the first repeating unit may include one repeating unit of Chemical Formula 1, one repeating unit of Chemical Formula 2, one repeating unit of Chemical Formula 3, or a mixture of two or more thereof. In addition, the second repeating unit may include one repeating unit of Chemical Formula 4, one repeating unit of Chemical Formula 5, or a mixture of two or more thereof.

The polymer may be prepared by curing a composition including reactive precursor compounds (monomers, oligomer, or polymers) capable of forming the first repeating unit and the second repeating unit, and the weight-average molecular weight of the polymer (measured by GPC) may be 5000 (MW) to 100,000 (MW).

The weight average molecular weight refers to a weight average molecular weight in terms of polystyrene measured by the GPC method, and g/mol may be used as a unit. In the process of measuring the weight average molecular weight in terms of polystyrene measured by the GPC method, a detector and an analytical column, such as a commonly known analysis apparatus and differential refractive index detector, can be used, and commonly applied temperature conditions, solvent, and flow rate can be used. Specific examples of the measurement conditions may include a temperature of 30° C., chloroform as a solvent, and a flow rate of 1 mL/min.

As the first repeating unit and the second repeating unit included in the polymer contain the divalent organic group represented by Chemical Formula 7, anisotropy can be produced by directly irradiating the light without a heat treatment process after the formation of the coating film, following by carrying out a heat treatment to complete the alignment film, and therefore, not only is it possible to prepare a liquid crystal alignment film capable of not only reducing a large amount of light irradiation energy, but also having an excellent aligning property and stability as well as a high voltage holding ratio and electrical characteristics.

The functional group containing a mesogenic group in the molecule may be presented by Chemical Formula 8 below:

wherein, in Chemical Formula 8,

Ar¹ and Ar² are each independently phenylene or naphthylene, Q¹ and Q² are a direct bond, an alkylene group having 1 to 10 carbon atoms, or an alkyleneoxy group having 1 to 10 carbon atoms, each L is independently a direct bond, —COO—, —C(CH₃)═CH—, or —C(CH₃)═N═N═C(CH₃)—, n is an integer of 0, 1, or 2, and m is an integer of 1 to 10 or an integer of 1 to 5.

For example, when Ar² is phenylene and m is 2, it may become a biphenylene functional group.

The alkyleneoxy group having 1 to 10 carbon atoms is a functional group in which an alkylene group having 1 to 10 carbon atoms and an ether group are bonded, and specifically, it may be represented by the formula —RO—. In this formula, R is an alkylene group having 1 to 10 carbon atoms.

Preferably, the functional group containing a mesogenic group in the molecule may be a functional group including an ester group in an aromatic ring in the molecule. Specifically, for example, in Chemical Formula 8, it may be a functional group, wherein Ar¹ and Ar² are each independently phenylene, Q¹ and Q² are each independently an alkyleneoxy group having 1 to 3 carbon atoms, L is —COO—, n is 1, and m is 1. More specifically, in Chemical Formula 8, it may be a functional group derived from 4-(oxiran-2-ylmethoxy)phenyl 4-(oxiran-2-ylmethoxy)benzoate where Ar¹ and Ar² are each independently phenylene, Q¹ and Q² are each independently a methyleneoxy group having 1 carbon atom, L is —COO—, and n is 1, the functional group being represented by Chemical Formula 8-1 below.

In addition, in Chemical Formula 8, it may be a functional group, wherein Ar¹ and Ar² are each independently phenylene, Q¹ and Q² are each independently an alkyleneoxy group having 1 to 3 carbon atoms, L is —COO—, n is 2, and m is 1. More specifically, in Chemical Formula 8, it may be a functional group derived from 1,4-phenylene bis(4-(oxiran-2-ylmethoxy)benzoate where Ar¹ and Ar² are each independently phenylene, Q¹ and Q² are each independently a methyleneoxy group having 1 carbon atom, L is —COO—, and n is 2, the functional group being represented by Chemical Formula 8-2 below.

As described above, in Chemical Formulae 4 and 5, as the functional group containing an ester group in an aromatic ring is used as the functional group containing a mesogenic group in the molecule, the liquid crystal aligning properties are enhanced, and accordingly, the retardation value of the liquid crystal cells prepared using the liquid crystal alignment film increases, thereby implementing excellent AC residual image properties.

Meanwhile, the polymer may further include a functional group represented by Chemical Formula 9 or a functional group represented by Chemical Formula 10 at at least one terminal end:

wherein, in Chemical Formula 9,

X¹, Y¹, and R′ and R″ are as defined in Chemical Formulae 1, 4, and 5,

wherein, in Chemical Formula 10,

R¹¹ and R¹² are each independently hydrogen or an alkyl group having 1 to 10 carbon atoms, and

X², Y², R′, and R″ are as defined in Chemical Formulae 2, 4 and 5.

Meanwhile, the polymer may further include a polymer containing a third repeating unit including at least one selected from the group consisting of Chemical Formulae 11 to 13; and a fourth repeating unit including at least one selected from the group consisting of Chemical Formulae 14 and 15:

wherein, in Chemical Formulae 11 to 15,

at least one of R¹³ and R¹⁴ is an alkyl group having 1 to 10 carbon atoms, and the other is hydrogen,

X⁶ to X¹⁰ are each independently a tetravalent organic group represented by Chemical Formula 6, and

Y⁶ to Y¹⁰ are each independently a divalent organic group represented by Chemical Formula 16 below:

wherein, in Chemical Formula 16,

R¹⁵ and R¹⁶ are each independently hydrogen, a halogen, a cyano, a nitrile, an alkyl having 1 to 10 carbon atoms, an alkenyl having 1 to 10 carbon atoms, an alkoxy having 1 to 10 carbon atoms, a fluoroalkyl having 1 to 10 carbon atoms, or a fluoroalkoxy having 1 to 10 carbon atoms,

p are q are each independently an integer of 0 to 4,

L² is a direct bond, —O—, —CO—, —S—, —SO₂—, —C(CH₃)₂—, —C(CF₃)₂—, —CONH—, —COO—, —(CH₂)_(y)—, —O(CH₂)_(y)O—, —O(CH₂)_(y)—, —NH—, —NH(CH₂)_(y)—NH—, —NH(CH₂)_(y)O—, —OCH₂—C(CH₃)₂—CH₂O—, —COO—(CH₂)_(y)—OCO—, or —OCO—(CH₂)_(y)—COO—,

y is an integer of 1 to 10,

k and m are each independently an integer of 0 to 3,

n is an integer of 0 to 3, and

R′ and R″ are as defined in Chemical Formulae 4 and 5.

In the liquid crystal alignment film, a weight ratio between the polymer containing the third repeating unit including at least one selected from the group consisting of Chemical Formula 11 to Chemical Formula 13, and the fourth repeating unit including at least one selected from the group consisting of Chemical Formula 14 and Chemical Formula 15 and the polymer containing the first repeating unit including at least one selected from the group consisting of Chemical Formula 1 to Chemical Formula 3 and the second repeating unit including at least one selected from the group consisting of Chemical Formula 4 and Chemical Formula 5, may be 10:90 to 90:10, 15:85 to 85:15, or 20:80 to 80:20.

Meanwhile, the polymer containing the third repeating unit including at least one selected from the group consisting of Chemical Formula 11 to Chemical Formula 13, and the fourth repeating unit including at least one selected from the group consisting of Chemical Formula 14 and Chemical Formula 15, is used for the liquid crystal alignment film in the state in which the polymer containing the first repeating unit including at least one selected from the group consisting of Chemical Formula 1 to Chemical Formula 3 and the second repeating unit including at least one selected from the group consisting of Chemical Formula 4 and Chemical Formula 5 is mixed, thereby significantly increasing the electrical characteristics of the alignment film such as the voltage holding ratio.

Meanwhile, the liquid crystal alignment film may have an AC brightness fluctuation rate of 3.5% or less, 0.1% to 3.5%, 2% to 3%, or 2.5% to 2.9%, which is represented by Mathematical Formula 1 below.

Brightness fluctuation rate (%)=[Initial brightness measured before driving the liquid crystal display device including the liquid crystal alignment film (L0)−Brightness measured after driving (L1)]/Initial brightness measured before driving (L0)×100  [Mathematical Formula 1]

In Mathematical Formula 1:

the initial brightness measured before driving the liquid crystal display device including the liquid crystal alignment film (L0) is a brightness in a black mode in which polarizing plates are adhered to the upper plate and the lower plate of the liquid crystal display device such that they are perpendicular to each other, and the polarizing plates are adhered to a backlight of 7000 cd/m²; and

the brightness measured after driving (L1) is a brightness in a black mode in which, after driving the liquid crystal display device at room temperature with an AC voltage of 5 V for 24 hours, polarizing plates are adhered to the upper plate and the lower plate of the liquid crystal display device such that they are perpendicular to each other, and the polarizing plates are adhered to a backlight of 7000 cd/m².

Examples of the preparation method of the liquid crystal display device including the liquid crystal alignment film are not particularly limited, and various preparation methods of liquid crystal display devices, which are previously known, can be applied. Preferably, a sealing agent impregnated with a ball spacer having a size of 3 μm is applied to the edge of the upper plate except at the liquid crystal injection hole, and the alignment films of the present invention formed on the upper plate and the lower plate are aligned such that they face each other and the alignment directions are aligned with each other, then the upper and lower plates are bonded together and the sealing agent is cured to prepare an empty space, and subsequently, a liquid crystal is injected into the empty cells to prepare an IPS mode liquid crystal cell.

Further, the liquid crystal alignment film may have a retardation value of 3 nm or higher, 4 nm or higher, 3 nm to 10 nm, 4 nm to 10 nm, 7 nm to 10 nm, or 7.9 nm to 8.7 nm. The retardation for the liquid crystal alignment film can be measured, for example, by irradiating a polarized light having a wavelength of 550 nm using AxoStep equipment, manufactured by Axometrics.

In general, the retardation of a birefringent material at a predetermined wavelength λ can be defined by the multiplication of birefringence at the wavelength Δη and the layer thickness d. At this time, the birefringence Δη can be obtained by the following Mathematical Formula 2.

Δη=η_(e)−η₀  [Mathematical Formula 2]

In Mathematical Formula 2, η₀ is defined as the refractive index in a direction having a constant speed regardless of the polarization direction of light, and η_(e) is defined as the refractive index in a direction having a different speed depending on the polarization direction.

The liquid crystal alignment film has a relatively high retardation value of 3 nm or higher, 4 nm or higher, 3 nm to 10 nm, 4 nm to 10 nm, 7 nm to 10 nm, or 7.9 nm to 8.7 nm. This is because the liquid crystal alignment film is prepared using the liquid crystal aligning composition in which an epoxy additive with a specific structure (for example, a benzoate-based epoxy) is mixed together with a polyimide precursor.

Specifically, the liquid crystal aligning agent composition described above is coated onto a substrate and dried to form a film, which is then directly irradiated with linearly polarized light without an imidization process to induce initial anisotropy, and subsequently, alignment of the reactive mesogenic epoxy present in the alignment film is initially induced through a low-temperature heat treatment, followed by carrying out an epoxy reaction to produce a reactive mesogenic liquid crystal film in the alignment film. Then, while carrying out a high-temperature heat treatment at a higher temperature than that of the low-temperature heat treatment to thereby proceed with imidization, the alignment stabilization can be achieved due to the anisotropy of the liquid crystal film prepared in the low-temperature heat treatment process. Accordingly, it is possible to prevent the occurrence of the residual image property while enhancing the film strength by using the reactive mesogenic epoxy.

The liquid crystal alignment film prepared according to the method for preparing a liquid crystal alignment as described above has features in that it not only exhibits excellent alignment properties, but also has excellent high-temperature AC brightness regulation, and in addition, it can maintain a high voltage holding ratio for a long period of time.

Furthermore, the liquid crystal alignment film may have a film strength of 2H or higher, 2H to 5H, or 3H to 4H. Examples of the method for measuring the film strength are not particularly limited, but for example, it can be measured by a pencil hardness tester according to the ASTM D3363 test standard by loading a weight of 50 g and using pencils of various hardnesses.

The liquid crystal alignment film can be prepared by the specific method for preparing a liquid crystal alignment film described below.

Method for Preparing Liquid Crystal Alignment Film

In addition, the present invention provides a method for preparing a liquid crystal alignment film including the steps of: 1) coating a liquid crystal aligning agent composition onto a substrate to form a coating film; 2) drying the coating film; 3) irradiating the coating film immediately after the drying step with light to perform alignment treatment; 4) subjecting the alignment-treated coating film to a low-temperature heat treatment at 200° C. or lower; and 5) subjecting the heat-treated coating film to heat treatment at a higher temperature than that of the low-temperature heat treatment to cure it, wherein the liquid crystal aligning agent composition includes: i) a first polymer for a liquid crystal aligning agent including at least two repeating units selected from the group consisting of a repeating unit represented by Chemical Formula 21, a repeating unit represented by Chemical Formula 22, and a repeating unit represented by Chemical Formula 23, wherein the repeating unit represented by Chemical Formula 21 is contained in an amount of 5 mol % to 74 mol % relative to the entire repeating units represented by Chemical Formulae 21 to 23; ii) a second polymer for a liquid crystal aligning agent including a repeating unit represented by Chemical Formula 24; and iii) a reactive mesogenic epoxy.

Coating a liquid crystal aligning agent composition onto a substrate to form a coating film (Step 1)

Step 1 is a step of coating a liquid crystal aligning agent composition onto a substrate to form a coating film. The liquid crystal aligning agent composition includes: i) a first polymer for a liquid crystal aligning agent including at least two repeating units selected from the group consisting of a repeating unit represented by Chemical Formula 21, a repeating unit represented by Chemical Formula 22, and a repeating unit represented by Chemical Formula 23, wherein the repeating unit represented by Chemical Formula 21 is included in an amount of 5 mol % to 74 mol % relative to the entire repeating units represented by Chemical Formulae 21 to 23; ii) a second polymer for a liquid crystal aligning agent including a repeating unit represented by Chemical Formula 24; and iii) a reactive mesogenic epoxy.

When a conventional polyimide is used as a liquid crystal alignment film, a polyimide precursor, a polyamic acid, or a polyamic acid ester having excellent solubility is coated and dried to form a coating film, which is then converted to a polyimide through a heat treatment process at a high temperature, to which light irradiation is performed, and to which alignment treatment is performed. However, a large amount of light irradiation energy is required for obtaining sufficient liquid crystal alignment properties by subjecting the layer in the form of polyimide to light irradiation, and additionally, an additional heat treatment process is undertaken for securing alignment stability after the light irradiation. Since the large amount of light irradiation energy and the additional high-temperature heat treatment process are very disadvantageous in view of the cost of the process and process time, a limitation in the application to a practical mass production process existed.

Accordingly, the present inventors found through experiments that, when the first polymer for the liquid crystal aligning agent, which essentially includes the repeating unit represented by Chemical Formula 21 and additionally includes at least one repeating unit selected from the group consisting of the repeating unit represented by Chemical Formula 22 and the repeating unit represented by Chemical Formula 23, and the second polymer for the liquid crystal aligning agent including the repeating unit represented by Chemical Formula 24, are mixed and used, the first polymer contains a certain amount of already imidized imide repeating units, and thus anisotropy can be produced by directly irradiating light without a heat-treatment process after the formation of the coating film, followed by carrying out a heat-treatment process to complete the alignment film, and therefore, it is possible to prepare a liquid crystal alignment film capable of not only reducing a large amount of light irradiation energy, but also having an excellent aligning property and stability as well as a high voltage holding ratio and electrical characteristics.

The first polymer for the liquid crystal aligning agent may include the repeating unit represented by Chemical Formula 21, which is an imide repeating unit, among the repeating units represented by Chemical Formula 21, Chemical Formula 22, and Chemical Formula 23, in an amount of 10 mol % to 74 mol %, preferably 20 mol % to 60 mol %, relative to the entire repeating units. As described above, when the first polymer for the liquid crystal including a specific amount of the imide repeating unit represented by Chemical Formula 21 is used, since the polymer includes a predetermined amount of already imidized imide repeating units, it is possible to prepare a liquid crystal alignment film having an excellent aligning property and stability as well as an excellent voltage holding ratio and electrical characteristics even when the light is directly irradiated without carrying out a heat-treatment process at a high temperature. When the repeating unit represented by Chemical Formula 21 is included at less than the content range above, sufficient aligning properties are not exhibited, and alignment stability may be deteriorated. When the content of the repeating unit represented by Chemical Formula 21 exceeds the range above, it may be difficult to prepare a stable alignment solution capable of coating due to low solubility. Accordingly, it is preferred to include the repeating unit represented by Chemical Formula 21 within the content range described above so as to provide a polymer for a liquid crystal aligning agent having excellent storage stability, electrical characteristics, aligning properties, and alignment stability.

Specifically, the imide-based functional group in L³ of Chemical Formula 26 above may a functional group represented by Chemical Formula 30 below:

wherein, in Chemical Formula 30,

Q is a tetravalent organic group derived from a hydrocarbon having 4 to 20 carbon atoms, or a tetravalent organic group in which at least one hydrogen in the tetravalent organic groups is substituted with a halogen or in which at least one —CH₂— is substituted with —O—, —CO—, —S—, —SO—, —SO₂—, or —CONH—, so that it may not be directly bonded to oxygen or sulfur atoms.

Further, the first polymer for the liquid crystal aligning agent may include the repeating unit represented by Chemical Formula 22 or the repeating unit represented by Chemical Formula 23 in an appropriate amount depending on the desired characteristics. Specifically, the repeating unit represented by Chemical Formula 22 may be included in an amount of 0 to 40 mol %, preferably 0 to 30 mol %, relative to the entire repeating units represented by Chemical Formulae 21 to 23. The repeating unit represented by Chemical Formula 22 has a low rate of conversion to imide during the high-temperature heat treatment process after the light irradiation, and thus if the above range is exceeded, the overall imidization rate is insufficient, thereby deteriorating the alignment stability. Accordingly, the repeating unit represented by Chemical Formula 22 exhibits appropriate solubility within the above-mentioned range and thus can provide a polymer for a liquid crystal aligning agent which can implement a high imidization rate, while having excellent processing properties. Furthermore, the repeating unit represented by Chemical Formula 23 may be contained in an amount of 0 to 95 mol %, preferably 10 to 90 mol %, relative to the entire repeating units represented by Chemical Formulae 21 to 23. Within such a range, excellent coating properties can be exhibited, thereby providing a polymer for a liquid crystal aligning agent which can implement a high imidization rate, while having excellent processing properties.

Meanwhile, the second polymer for the liquid crystal aligning agent is mixed with the first polymer for the liquid crystal aligning agent, which is a partially imidized polymer, and used as a liquid crystal aligning agent, and thus can significantly enhance the electrical characteristics of an alignment film such as the voltage holding ratio as compared to the case where only the first polymer for the liquid crystal aligning agent is used.

In order to exhibit such an effect, it is preferred that X¹⁴ in the repeating unit represented by Chemical Formula 24 is derived from an aromatic structure in view of improving the voltage holding ratio.

In addition, in the repeating unit represented by Chemical Formula 24, it is preferred that Y¹⁴ is a bivalent organic group represented by Chemical Formula 26. Herein, R³⁰ and R³¹ are each independently a short-chain functional group having 3 or less carbon atoms, or it is more preferable that R³⁰ and R³¹, which are branched structures, are not included (h and i are 0).

Preferably, the Q, X¹², X¹³, and X¹⁴ are each independently a tetravalent organic group represented by Chemical Formula 27 below:

wherein, in Chemical Formula 27,

R³² to R³⁵ are each independently hydrogen or a C₁₋₆ alkyl,

L⁴ is a single bond, —O—, —CO—, —S—, —C(CH₃)₂—, —C(CF₃)₂—, —CONH—, —COO—, —(CH₂)_(z)—, —O(CH₂)_(z)O—, or —COO—(CH₂)_(z)—OCO—, and

z is an integer of 1 to 10.

Further, the first polymer for the liquid crystal aligning agent and the second polymer for the liquid crystal aligning agent may be mixed in a weight ratio of about 15:85 to 85:15, preferably about 20:80 to 80:20. As described above, the first polymer for the liquid crystal aligning agent includes a certain amount of already imidized imide repeating units, and thus it has a feature in that anisotropy can be produced by directly irradiating the light without a high-temperature heat treatment process after the formation of the coating film, followed by carrying out a heat treatment to complete the alignment film. The second polymer for the liquid crystal aligning agent has a feature in that it can enhance the electrical characteristics such as the voltage holding rate. When the first polymer for the liquid crystal aligning agent and the second polymer for the liquid crystal aligning agent having such characteristics are mixed in the weight ratio range above and used, the excellent photo-reaction characteristics and liquid crystal alignment properties of the first polymer for the liquid crystal aligning agent and the excellent electrical characteristics of the second polymer for the liquid crystal aligning agent can complement each other, and thus a liquid crystal alignment film simultaneously having excellent alignment properties and electrical characteristics can be prepared.

In addition to the first polymer for the liquid crystal aligning agent and the second polymer for the liquid crystal aligning agent described above, the liquid crystal aligning agent composition according to the present invention includes a reactive mesogenic epoxy, and thus it is possible to improve the film strength of the liquid crystal alignment film prepared therefrom.

The reactive mesogenic epoxy refers to a compound in which a glycidyl group is substituted at both terminals of a mesogenic group. Specifically, the reactive mesogenic epoxy may be a compound represented by Chemical Formula 28 below:

R³⁶-MG-R³⁶  [Chemical Formula 28]

wherein, in Chemical Formula 28,

R³⁶ is glycidyloxy or N(glycidyloxy)₂, and

MG is a divalent mesogenic group.

Preferably, the MG is represented by Chemical Formula 29 below:

wherein, in Chemical Formula 29,

Ar₃ and Ar₄ are each independently phenylene or naphthylene,

each L⁵ is independently a single bond, an alkylene having 1 to 3 carbon atoms, —COO—, —C(CH₃)═CH—, or —C(CH₃)═N═N═C(CH₃)—,

-   -   n is 0, 1, or 2, and m is an integer of 1 to 10 or an integer of         1 to 5.

For example, when Ar₄ is phenylene and m is 2, it may become a biphenylene functional group.

More preferably, the MG is any one selected from the group listed below.

In addition, it is preferable that the reactive mesogenic epoxy is contained in an amount of 0.1% by weight to 30% by weight relative to the total weight of the first polymer for the liquid crystal aligning agent and the second polymer for the liquid crystal aligning agent described above.

Meanwhile, the method of coating the liquid crystal aligning agent composition onto a substrate is not particularly limited, and for example, a method such as screen printing, offset printing, flexographic printing, inkjet printing, and the like can be used.

Furthermore, the liquid crystal aligning agent composition may be a composition in which the first polymer for the liquid crystal aligning agent and the second polymer for the liquid crystal aligning agent are dissolved or dispersed in an organic solvent. Specific examples of the organic solvent include N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidone, N-methylcaprolactam, 2-pyrrolidone, N-ethylpyrrolidone, N-vinylpyrrolidone, dimethylsulfoxide, tetramethylurea, pyridine, dimethyl sulfone, hexamethyl sulfoxide, γ-butyrolactone, 3-methoxy-N,N-dimethylpropanamide, 3-ethoxy-N,N-dimethylpropanamide, 3-butoxy-N,N-dimethylpropanamide, 1,3-dimethyl-imidazolidinone, ethyl amyl ketone, methyl nonyl ketone, methyl ethyl ketone, methyl isoamyl ketone, methyl isopropyl ketone, cyclohexanone, ethylene carbonate, propylene carbonate, diglyme, 4-hydroxy-4-methyl-2-pentanone, ethylene glycol monomethyl ether, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether, ethylene glycol monoethyl ether acetate, ethylene glycol monopropyl ether, ethylene glycol monopropyl ether acetate, ethylene glycol monoisopropyl ether, ethylene glycol monoisopropyl ether acetate, ethylene glycol monobutyl ether, ethylene glycol monobutyl ether acetate, and the like. They can be used alone or in combination.

In addition, the liquid crystal aligning agent composition may further include other components in addition to the polymers for the liquid crystal aligning agent and the organic solvent. In a non-limiting example, when the liquid crystal aligning agent composition is coated, an additive capable of improving the uniformity of the thickness of a layer and or surface smoothness, improving the adhesion between a photo-alignment film and a substrate, changing the dielectric constant or conductivity of a photo-alignment film, or increasing the denseness of a photo-alignment film may further be included. Examples of such additives include various solvents, surfactants, silane-based compounds, dielectrics, crosslinking compounds, etc.

Drying the Coating Film (Step 2)

Step 2 is a step of drying the coating film prepared in Step 1.

The step of drying the coating film is for removing a solvent or the like used in the liquid crystal aligning agent composition, and for example, a method such as heating of a coating film or vacuum evaporation may be used. The drying may be preferably carried out at 50 to 130° C., and more preferably at 70 to 120° C.

Irradiating the Coating Film with Light Immediately after the Drying Step to Perform Alignment Treatment (Step 3)

Step 3 is a step of irradiating the coating film dried in Step 2 with light to perform alignment treatment.

In the present specification, the “irradiating the film immediately after the drying step” refers to irradiating the light immediately after the drying step without carrying out a heat treatment at a temperature equal to or higher than that of the drying step, and other steps in addition to the heat treatment can be added.

More specifically, when a liquid crystal alignment film is prepared using a conventional liquid crystal aligning agent including polyamic acid or polyamic acid ester, it includes a step of irradiating light after essentially carrying out a high-temperature heat treatment for imidization of the polyamic acid. However, when a liquid crystal alignment film is prepared using the liquid crystal aligning agent of one embodiment described above, it does not include the heat treatment step, but light is directly irradiated to perform alignment treatment, and then the alignment-treated coating film is cured by a heat treatment, thereby preparing a liquid crystal alignment film having sufficient alignment properties and improved stability even under a small amount of light irradiation energy.

In addition, in the alignment treatment step, the light irradiation is preferably performed by irradiating polarized ultraviolet light having a wavelength of 150 to 450 nm. Herein, the intensity of the light exposure varies depending on the kind of the polymer for the liquid crystal aligning agent, and preferably energy of 10 mJ/cm² to 10 J/cm², and more preferably energy of 30 mJ/cm² to 2 J/cm², may be irradiated. As for the ultraviolet light, polarized ultraviolet light selected from the ultraviolet light subjected to polarization treatment through a method of penetrating or reflecting (1) a polarizing device using a substrate coated with a dielectric anisotropic material on the surface of a transparent substrate such as quartz glass, soda lime glass, soda lime free glass, etc., (2) a polarizer plate on which aluminum or metal wires are finely deposited, or (3) a Brewster's polarizing device using reflection of quartz glass, etc., are irradiated to perform the alignment treatment. Herein, the polarized ultraviolet light may be irradiated perpendicularly to the surface of the substrate, or may be irradiated by directing an angle of incidence at a specific angle. By this method, the alignment ability of the liquid crystal molecules is imparted to the coating film.

Subjecting the Alignment-Treated Coating Film to Low-Temperature Heat Treatment (Step 4)

Step 4 is a step of subjecting the alignment-treated coating film in Step 3 to a low-temperature heat treatment.

As described above, since the initial anisotropy is induced by directly irradiating linearly polarized light without an imidization process in Step 3, this is a step of re-aligning a part of the alignment film and initially inducing alignment of the reactive mesogenic epoxy present in the alignment film through a low-temperature heat treatment, followed by carrying out an epoxy reaction to prepare a reactive mesogenic liquid crystal film in the alignment film. Further, such a low-temperature heat treatment step is distinguished from the step of curing the alignment-treated coating film by heat treatment to be described later.

The temperature for the low-temperature heat treatment is preferably 200° C. or lower. Preferably, the temperature for the low-temperature heat treatment is 110 to 200° C., and more preferably 130 to 180° C. Herein, the means of the heat treatment is not particularly limited, and may be carried out by a heating means such as a hot plate, a hot air circulation path, an infrared ray furnace, and the like.

Subjecting the Heat-Treated Coating Film to Heat Treatment at a Higher Temperature than that of the Low-Temperature Heat Treatment to Cure it (Step 5)

Step 5 is a step of subjecting the coating film heat-treated at a low temperature in Step 4 to a high-temperature heat treatment to cure it.

The step of subjecting the alignment-treated coating film to a heat treatment to cure it is a step that is carried out after the irradiation of light even in the method for preparing a liquid crystal alignment film using a polymer for a liquid crystal aligning agent including a conventional polyamic acid or polyamic acid ester, and is distinguished from the heat treatment step which is carried out for the imidization of the liquid crystal aligning agent composition after coating the liquid crystal aligning agent composition onto a substrate and before irradiating the light or while irradiating the light.

In addition, the epoxy reaction of the reactive mesogenic epoxy is carried out, and thus the alignment stabilization can be improved. Accordingly, the temperature for the heat treatment is a temperature at which the imidization of the polymers for the liquid crystal aligning agent and the epoxy reaction of the reactive mesogenic epoxy are carried out, and is preferably higher than the temperature for the low temperature heat treatment of Step 4. Preferably, the temperature for the heat treatment is carried out at 200 to 250° C., and more preferably at 210 to 240° C. Herein, the means of the heat treatment is not particularly limited, and may be carried out by a heating means such as a hot plate, a hot air circulation path, an infrared ray furnace, and the like.

Liquid Crystal Display Device

In addition, the present invention provides a liquid crystal display device including the liquid crystal alignment film described above.

The liquid crystal alignment film may be introduced into a liquid crystal cell by a known method, and likewise, the liquid crystal cell may be introduced into a liquid crystal display device by a known method. Examples of the preparation method of the liquid crystal display device including the liquid crystal alignment film are not particularly limited, but various preparation methods of the liquid crystal display device, which are previously known, can be applied. Preferably, a sealing agent impregnated with a ball spacer having a size of 3 μm is applied to the edge of the upper plate except the liquid crystal injection hole, and the alignment films of the present invention formed on the upper plate and the lower plate are aligned such that they face each other and the alignment directions are aligned with each other, and then the upper and lower plates are bonded together and the sealing agent is cured to prepare an empty space. Subsequently, a liquid crystal is injected into the empty cells to produce a parallel-alignment mode liquid crystal cell.

Advantageous Effects

According to the present invention, a liquid crystal alignment film not only having excellent alignment property and stability, but also having high film strength, and thus exhibiting excellent durability and a high residual image property, a method for preparing the same, and a liquid crystal display device using the same can be prepared.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Hereinafter, the present invention will be described in more detail by way of examples. However, these examples are given for illustrative purposes only, and the scope of the invention is not intended to be limited by these examples.

Preparation Example 1: Synthesis of Diamine

Cyclobutane-1,2,3,4-tetracarboxylic dianhydride (CBDA) and 4-nitroaniline were dissolved in DMF (dimethylformamide) to prepare a mixture. Then, the mixture was reacted at about 80° C. for about 12 hours to prepare an amic acid. Subsequently, the amic acid was dissolved in DMF, and acetic anhydride and sodium acetate were added thereto to prepare a mixture. Then, the amic acid contained in the mixture was imidized at about 90° C. for about 4 hours. The thus-obtained imide was dissolved in DMAc (dimethylacetamide), and then Pd/C was added thereto to prepare a mixture. The mixture was reduced at 45° C. under hydrogen pressure of 6 bar for 20 minutes to prepare a diamine

Preparation Example 2: Preparation of Polymer for Liquid Crystal Aligning Agent P-1

(Step 1)

5.0 g (13.3 mmol) of the diamine prepared in Preparation Example 1 was completely dissolved in 71.27 g of anhydrous N-methyl pyrrolidone (NMP).

Then, 2.92 g (13.03 mmol) of 1,3-dimethyl-cyclobutane-1,2,3,4-tetracarboxylic dianhydride was added to the solution under an ice bath and stirred at room temperature for 16 hours.

(Step 2)

The solution obtained in Step 1 was poured into an excess amount of distilled water to form a precipitate. Then, the formed precipitate was filtered and washed twice with distilled water and three times with methanol. The thus-obtained solid product was dried in a vacuum oven at 40° C. for 24 hours to obtain 6.9 g of a polymer for a liquid crystal aligning agent P-1.

As a result of confirming the molecular weight of P-1 through GPC, the number average molecular weight (Mn) was 15,500 g/mol, and the weight average molecular weight (Mw) was 31,000 g/mol. Further, the monomer structure of the polymer P-1 was determined by the equivalent ratio of the monomers used, and the ratio of the imine structure in the molecule was 50.5%, while the ratio of the amic acid structure was 49.5%.

Preparation Example 3: Preparation of Polymer for Liquid Crystal Aligning Agent Q-1

5.00 g of 4,4′-methylenedianiline and 5.05 g of 4,4′-oxydianiline were completely dissolved in 221.4 g of NMP. Then, 14.55 g of 4,4′-biphthalic anhydride was added to the solution under an ice bath and stirred at room temperature for 16 hours. Subsequently, the polymer Q-1 was prepared in the same manner as in Step 2 of Preparation Example 2.

Example 1

(1) Preparation of Liquid Crystal Aligning Agent Composition

5 parts by weight of P-1 prepared in Preparation Example 2, 5 parts by weight of Q-1 prepared in Preparation Example 3, and 0.8 parts by weight of 4-(oxiran-2-ylmethoxy)phenyl 4-(oxiran-2-ylmethoxy)benzoate (8% by weight relative to the polymer for the liquid crystal aligning agent) were completely dissolved in a mixed solvent of NMP and n-butoxyethanol in a weight ratio of 8:2. Then, the resultant was subjected to pressure filtration with a filter made of poly(tetrafluoroethylene) having a pore size of 0.2 μm to prepare a liquid crystal aligning agent composition.

(2) Preparation of Liquid Crystal Alignment Film

The liquid crystal aligning agent composition prepared in Example 1 was coated onto a substrate (lower plate) in which comb-shaped IPS mode-type ITO electrode patterns having a thickness of 60 nm, an electrode width of 3 μm, and spacing between the electrodes of 6 μm are formed on a rectangular glass substrate having a size of 2.5 cm×2.7 cm and onto a glass substrate (upper plate) having no electrode pattern each using a spin coating method.

Then, the substrates onto which the liquid crystal aligning agent composition was coated were placed on a hot plate at about 80° C. for one minute to evaporate the solvent. In order to align the thus-obtained coating film, ultraviolet light of 254 nm was irradiated with an intensity of 0.3 J/cm² using an exposure apparatus in which a linear polarizer was adhered to the coating film of each of the upper and lower plates.

Subsequently, the coating film was placed on a hot plate at 130° C. for 500 seconds, thereby subjecting it to a low-temperature heat treatment. Then, the coating film was calcinated (cured) in an oven at about 230° C. for 20 minutes to obtain a liquid crystal alignment film having a film thickness of 0.1 μm.

Example 2

A liquid crystal aligning agent composition and liquid crystal alignment film were prepared in the same manner as in Example 1, except that 4-(oxiran-2-ylmethoxy)phenyl 4-(oxiran-2-ylmethoxy)benzoate was used in an amount of 1.0 part by weight (10% by weight relative to the polymer for the liquid crystal aligning agent).

Example 3

A liquid crystal aligning agent composition and liquid crystal alignment film were prepared in the same manner as in Example 1, except that 1,4-phenylene bis(4-(oxiran-2-ylmethoxy)benzoate) was used instead of 4-(oxiran-2-ylmethoxy)phenyl 4-(oxiran-2-ylmethoxy)benzoate.

Comparative Example 1

A liquid crystal aligning agent composition and liquid crystal alignment film were prepared in the same manner as in Example 1, except that the following compound (BATG) was used instead of 4-(oxiran-2-ylmethoxy)phenyl 4-(oxiran-2-ylmethoxy)benzoate.

Comparative Example 2

A liquid crystal aligning agent composition and liquid crystal alignment film were prepared in the same manner as in Example 1, except that the following compound (CDMDG) was used instead of 4-(oxiran-2-ylmethoxy)phenyl 4-(oxiran-2-ylmethoxy)benzoate.

Comparative Example 3

A liquid crystal aligning agent composition and liquid crystal alignment film were prepared in the same manner as in Example 1, except that the low-temperature heat treatment was omitted and the calcination (curing) temperature was adjusted to 240° C.

Comparative Example 4

A liquid crystal aligning agent composition and liquid crystal alignment film were prepared in the same manner as in Example 2, except that the low-temperature heat treatment was omitted and the calcination (curing) temperature was adjusted to 240° C.

Comparative Example 5

A liquid crystal aligning agent composition and liquid crystal alignment film were prepared in the same manner as in Example 1, except that 4-(oxiran-2-ylmethoxy)phenyl 4-(oxiran-2-ylmethoxy)benzoate was not used.

Experimental Example

A sealing agent impregnated with a ball spacer having a size of 3 μm was applied to the edge of the upper plate except the liquid crystal injection hole. Further, the alignment films of the examples and comparative examples formed on the upper plate and the lower plate were aligned such that they faced each other and the alignment directions were aligned with each other, and then the upper and lower plates were bonded together and the sealing agent was cured to prepare an empty space. Subsequently, a liquid crystal was injected into the empty cells to produce a parallel-alignment mode liquid crystal cell.

(1) Retardation (R)

The retardation (R) of the liquid crystal alignment films obtained in the examples and comparative examples was measured. Specifically, each retardation was measured by irradiating polarized light having a wavelength of 550 nm using AxoStep equipment, manufactured by Axometrics, and the average value of the measured values for 5 repeated measurements is shown in Table 1 below.

(2) Film Strength

The film strength for the alignment films obtained in the examples and comparative examples was measured, and the results are shown in Table 1 below. Specifically, the film strength of the alignment films was measured via a pencil hardness tester according to the ASTM D3363 test standard by loading a weight of 50 g and using pencils of various hardnesses.

(3) Brightness Fluctuation Rate

The brightness fluctuation rate of the prepared liquid crystal cells was measured using the liquid crystal alignment films obtained in the examples and comparative examples. Specifically, polarizing plates were adhered to the upper plate and the lower plate of the liquid crystal cells such that they were perpendicular to each other. Then, the liquid crystal cells, to which the polarizing plates were adhered, were adhered onto a backlight of 7000 cd/m², and the brightness in a black mode was measured using PR-880 equipment, which is a device for measuring brightness. Then, the liquid crystal cells were driven at room temperature for 24 hours with an AC voltage of 5 V. Subsequently, the brightness in a black mode was measured in the same manner as described above in a state in which the voltage of the liquid crystal cells was turned off, and the results are shown in Table 1 below.

The difference between the initial luminance (L0) measured before driving the liquid crystal cell and the luminance (L1) measured after driving was divided by the initial luminance (L0) and multiplied by 100 to calculate the brightness fluctuation rate. As the thus-calculated brightness fluctuation rate is closer to 0%, it means that the alignment stability is excellent.

TABLE 1 Retar- Brightness Epoxy dation Film fluctuation Category additives (nm) strength rate Example 1 A-1 8.3 3H 2.7% (8% by weight relative to the polymer for the liquid crystal aligning agent) Example 2 A-1 7.9 4H 2.9% (10% by weight relative to the polymer for the liquid crystal aligning agent) Example 3 A-2 8.7 3H 2.5% (8% by weight relative to the polymer for the liquid crystal aligning agent) Comparative B-1 2.6 3H 8.4% Example 1 (8% by weight relative to the polymer for the liquid crystal aligning agent) Comparative B-2 2.4 3H   7% Example 2 (8% by weight relative to the polymer for the liquid crystal aligning agent) Comparative A-1 2.3 3H   4% Example 3 (8% by weight relative to the polymer for the liquid crystal aligning agent) Comparative A-1 2.8 4H   6% Example 4 (10% by weight relative to the polymer for the liquid crystal aligning agent) Comparative — 3.9 0H 2.1% Example 5 *A-1: 4-(oxiran-2-ylmethoxy)phenyl 4-(oxiran-2-ylmethoxy)benzoate *A-2: 1,4-phenylene bis(4-(oxiran-2-ylmethoxy)benzoate) *B-1: BATG

*B-2: CDMDG

As shown in Table 1 above, when the epoxy additives with different structures compared to those of the examples were used similarly to Comparative Examples 1 and 2, it was confirmed that the retardation value was significantly lower than those of the examples, and the brightness fluctuation rate was increased. From this, it was confirmed that, in the case of the liquid crystal alignment films obtained by using the phenyl benzoate-based RM (reactive mesogen) epoxy additive, the retardation is increased, thereby implementing excellent AC residual image properties, and also the brightness fluctuation rate is reduced, thereby implementing excellent aligning stability.

In addition, in Table 1, similarly to Comparative Examples 3 and 4, although the same amount of the phenyl benzoate-based epoxy additive was used, when the low-temperature heat treatment was omitted and the calcination (curing) temperature was adjusted to 240° C., it was confirmed that the retardation value was significantly lower than those of the examples, and the brightness fluctuation rate was increased. From this, it was confirmed that, similarly to the examples, as curing was carried out after heat treatment, the retardation of the finally prepared alignment film is increased, thereby implementing excellent AC residual properties, and also the brightness fluctuation rate is reduced, thereby implementing excellent aligning stability.

Meanwhile, similarly to Comparative Example 5, when no phenyl benzoate-based epoxy additives were added, it was confirmed that the film strength was significantly reduced compared to those of the examples, and thus the strength of the liquid crystal alignment films can be enhanced by using the specific epoxy additives in the examples. 

1-8. (canceled)
 9. A method for preparing a liquid crystal alignment film including the steps of: 1) coating a liquid crystal aligning agent composition onto a substrate to form a coating film; 2) drying the coating film; 3) irradiating the coating film with light immediately after the drying step to perform alignment treatment; 4) subjecting the alignment-treated coating film to a low-temperature heat treatment at 200° C. or lower; and 5) subjecting the heat-treated coating film to heat treatment at a higher temperature than that of the low-temperature heat treatment to cure it, wherein the liquid crystal aligning agent composition includes: i) a first polymer for a liquid crystal aligning agent including at least two repeating units selected from the group consisting of a repeating unit represented by Chemical Formula 21 below, a repeating unit represented by Chemical Formula 22 below, and a repeating unit represented by Chemical Formula 23 below, wherein the repeating unit represented by Chemical Formula 21 below is contained in an amount of 5 mol % to 74 mol % relative to the entire repeating units represented by Chemical Formulae 21 to 23 below; ii) a second polymer for a liquid crystal aligning agent including a repeating unit represented by Chemical Formula 24 below; and iii) a reactive mesogenic epoxy:

wherein, in Chemical Formulae 21 to 24, R²² and R²³ are each independently hydrogen or a C₁₋₁₀ alkyl, with the proviso that R²² and R²³ are not all hydrogen, R²⁴ and R²⁵ are each independently hydrogen or a C₁₋₁₀ alkyl, and X¹¹ is a tetravalent organic group represented by Chemical Formula 25 below:

wherein, in Chemical Formula 25, R²⁶ to R²⁹ are each independently hydrogen or a C₁₋₆ alkyl, X¹², X¹³, and X¹⁴ are each independently a tetravalent organic group derived from a hydrocarbon having 4 to 20 carbon atoms, or a tetravalent organic group in which at least one hydrogen in the tetravalent organic groups is substituted with a halogen or in which at least one —CH₂— is substituted with —O—, —CO—, —S—, —SO—, —SO₂—, or —CONH—, so that it is not directly bonded to oxygen or sulfur atoms, and Y¹¹, Y¹², Y¹³, and Y¹⁴ are each independently a divalent organic group represented by Chemical Formula 26 below:

wherein, in Chemical Formula 26, R³⁰ and R³¹ are each independently a halogen, a cyano, a C₁₋₁₀ alkyl, a C₂₋₁₀ alkenyl, a C₁₋₁₀ alkoxy, a C₁₋₁₀ fluoroalkyl, or a C₁₋₁₀ fluoroalkoxy, h and i are each independently an integer of 0 to 4, L³ is a single bond, —O—, —CO—, —S—, —SO₂—, —C(CH₃)₂ ⁻, —C(CF₃)₂—, —CONH—, —COO—, —(CH₂)_(z)—, —O(CH₂)_(z)O—, —O(CH₂)_(z)—, —OCH₂—C(CH₃)₂—CH₂O—, —COO—(CH₂)_(z)—OCO—, or —OCO—(CH₂)_(z)—COO—, z is an integer of 1 to 10, and j is an integer of 0 to
 3. 10. The method for preparing a liquid crystal alignment film of claim 9, wherein the X¹², X¹³, and X¹⁴ are each independently a tetravalent organic group represented by Chemical Formula 27 below:

wherein, in Chemical Formula 27, R³² to R³⁵ are each independently hydrogen or a C₁₋₆ alkyl, L⁴ is a single bond, —O—, —CO—, —S—, —C(CH₃)₂—, —C(CF₃)₂—, —CONH—, —COO—, —(CH₂)_(z)—, —O(CH₂)_(z)O—, or —COO—(CH₂)_(z)—OCO—, and z is an integer of 1 to
 10. 11. The method for preparing a liquid crystal alignment film of claim 9, wherein the reactive mesogenic epoxy is represented by Chemical Formula 28 below: R³⁶-MG-R³⁶  [Chemical Formula 28] wherein, in Chemical Formula 28, R³⁶ is glycidyloxy or N(glycidyloxy)₂, and MG is a divalent mesogenic group.
 12. The method for preparing a liquid crystal alignment film of claim 11, wherein the MG is represented by Chemical Formula 29 below:

wherein, in Chemical Formula 29, Ar₃ and Ar₄ are each independently phenylene or naphthylene, each L⁵ is independently a single bond, an alkylene having 1 to 3 carbon atoms, —COO—, —C(CH₃)═CH—, or —C(CH₃)═N═N═C(CH₃)—, n is 0, 1, or 2, and m is an integer of
 1. 13. The method for preparing a liquid crystal alignment film of claim 11, wherein the MG is any one selected from the groups listed below:


14. The method for preparing a liquid crystal alignment film of claim 9, wherein the mesogenic epoxy is included in an amount of 0.1% by weight to 30% by weight relative to the weight of the polymers for the liquid crystal aligning agent.
 15. The method for preparing a liquid crystal alignment film of claim 9, wherein the first polymer for the liquid crystal aligning agent and the second polymer for the liquid crystal aligning agent may be mixed in a weight ratio of 15:85 to 85:15.
 16. The method for preparing a liquid crystal alignment film of claim 9, wherein the drying of Step 2 is performed at 50° C. to 130° C.
 17. The method for preparing a liquid crystal alignment film of claim 9, wherein the alignment treatment of Step 3 is performed by irradiating polarized ultraviolet light having a wavelength of 150 nm to 450 nm.
 18. The method for preparing a liquid crystal alignment film of claim 9, wherein the low-temperature heat treatment of Step 4 is performed at 110° C. to 200° C.
 19. The method for preparing a liquid crystal alignment film of claim 9, wherein the heat treatment of Step 5 is performed at 200° C. to 250° C.
 20. (canceled) 